Objective: The aim of this study was to evaluate the effect of finishing time and polishing time on surface roughness and microhardness of nanofilled and hybrid resin composites.
Materials and methods: Hundred disk composite specimens from micro hybrid composite and nanohybrid composite were prepared, 50 for each type of composite. The specimens were divided into five groups according to the time of finishing and polishing (immediate, 15 min, 24 h and dry). Composite under the Mylar strip without finishing and polishing was taken as the control group. Surface roughness was measured with environmental scanning electronic microscope (ESEM) and microhardness was determined using Vickers Microhardness Tester. Data collected were statistically analyzed by t-test and one-way analysis of variance (ANOVA) followed by Turkey's post hoc test.
Results: Smooth surface with low hardness was obtained for the group under Mylar strip without finishing and polishing. The highest roughness was recorded for delayed finishing and polishing for both composites. Immediate finishing and polishing increased the surface hardness more than that in the control group in both types of composites. Dry finishing reduced the hardness significantly for micro hybrid composite, but resulted in the highest surface hardness for nanofilled composite.
Conclusion: Immediate finishing and polishing under coolant resulted in the best surface smoothness and hardness values in micro hybrid composite; however, immediate dry finishing and polishing gave the best smoothness and hardness values in nanohybrid composite.
Keywords: Microhardness; resin composite; roughness.