Increment of specific heat capacity of solar salt with SiO2 nanoparticles

Patricia Andreu-Cabedo; Rosa Mondragon; Leonor Hernandez; Raul Martinez-Cuenca; Luis Cabedo; J Enrique Julia

doi:10.1186/1556-276X-9-582

Increment of specific heat capacity of solar salt with SiO2 nanoparticles

Nanoscale Res Lett. 2014 Oct 20;9(1):582. doi: 10.1186/1556-276X-9-582. eCollection 2014.

Authors

Patricia Andreu-Cabedo¹, Rosa Mondragon¹, Leonor Hernandez¹, Raul Martinez-Cuenca¹, Luis Cabedo², J Enrique Julia¹

Affiliations

¹ Departamento de Ingeniería Mecánica y Construcción, Universitat Jaume I. Campus de Riu Sec, Castellón de la Plana, Spain.
² Polymers and Advanced Materials Group (PIMA), Universitat Jaume I. Campus de Riu Sec, Castellón de la Plana, Spain.

Abstract

Thermal energy storage (TES) is extremely important in concentrated solar power (CSP) plants since it represents the main difference and advantage of CSP plants with respect to other renewable energy sources such as wind, photovoltaic, etc. CSP represents a low-carbon emission renewable source of energy, and TES allows CSP plants to have energy availability and dispatchability using available industrial technologies. Molten salts are used in CSP plants as a TES material because of their high operational temperature and stability of up to 500°C. Their main drawbacks are their relative poor thermal properties and energy storage density. A simple cost-effective way to improve thermal properties of fluids is to dope them with nanoparticles, thus obtaining the so-called salt-based nanofluids. In this work, solar salt used in CSP plants (60% NaNO3 + 40% KNO3) was doped with silica nanoparticles at different solid mass concentrations (from 0.5% to 2%). Specific heat was measured by means of differential scanning calorimetry (DSC). A maximum increase of 25.03% was found at an optimal concentration of 1 wt.% of nanoparticles. The size distribution of nanoparticle clusters present in the salt at each concentration was evaluated by means of scanning electron microscopy (SEM) and image processing, as well as by means of dynamic light scattering (DLS). The cluster size and the specific surface available depended on the solid content, and a relationship between the specific heat increment and the available particle surface area was obtained. It was proved that the mechanism involved in the specific heat increment is based on a surface phenomenon. Stability of samples was tested for several thermal cycles and thermogravimetric analysis at high temperature was carried out, the samples being stable.

Pacs: 65.: Thermal properties of condensed matter; 65.20.-w: Thermal properties of liquids; 65.20.Jk: Studies of thermodynamic properties of specific liquids.

Keywords: Nanofluid; Solar salt; Specific heat capacity; Thermal energy storage.