Purpose: The aims of this randomized-controlled clinical trial were to compare marginal and internal adaptation of all-ceramic crowns fabricated with CAD/CAM and heat-pressed (HP) techniques before luting and to evaluate the clinical outcomes at baseline and at 6, 12, and 24 months after luting.
Materials and methods: Fifteen CAD/CAM (CC) and 15 HP all-ceramic crowns were placed in 15 patients. A silicone replica was obtained to measure marginal and internal adaptation of each all-ceramic crown before luting, and they were sectioned buccolingually and mesiodistally. Marginal and internal adaptations were measured using computerized light microscope at 40× magnification. Clinical evaluations took place at baseline (2 days after luting) and at 6, 12, and 24 months after luting. Replica scores were analyzed with Mann-Whitney U and Student's t-test (α = 0.05). Survival rate of crowns was determined using Kaplan-Meier statistical analysis.
Results: The median marginal gap for the CC group was 132.2 μm and was 130.2 μm for the HP group. The mean internal adaptation for the CC group was 220.3 ± 51.3 μm and 210.5 ± 31 μm for the HP group. There were no statistically significant differences with respect to marginal opening (Mann-Whitney U test; p = 0.95) and internal adaptation (Student's t-test; p = 0.535) between the 2 groups. Based on modified Ryge criteria, 100% of the crowns were rated satisfactory during the 2-year period.
Conclusion: In this in vivo study, CAD/CAM and HP all-ceramic crowns exhibited similar marginal and internal adaptations. A 100% success rate was recorded for the 15 CAD/CAM and for the 15 HP all-ceramic crowns during the 2-year period.
Keywords: All-ceramic; CAD/CAM; heat-pressed; internal adaptation; marginal adaptation.