The Ni-yttria-stabilized zirconia (YSZ) anode functional layer in solid oxide fuel cells produced by pulsed laser-deposition was studied using three-dimensional tomography. Anode feature sizes of ~130 nm were quite small relative to typical anodes, but errors arising in imaging and segmentation were shown using a sensitivity analysis to be acceptable. Electrochemical characterization showed that these cells achieved a relatively high maximum power density of 1.4 W cm(-2) with low cell resistance at an operating temperature of 600 °C. The tomographic data showed anode three-phase boundary density of ~56 μm(-2), more than 10 times the value observed in conventional Ni-YSZ anodes. Anode polarization resistance values, predicted by combining the structural data and literature values of three-phase boundary resistance in an electrochemical model, were consistent with measured electrochemical impedance spectra, explaining the excellent intermediate-temperature performance of these cells.