Li3PO4-coated LiNi0.5Mn1.5O4: a stable high-voltage cathode material for lithium-ion batteries

Abstract

LiNi0.5Mn1.5O4 is regarded as a promising cathode material to increase the energy density of lithium-ion batteries due to the high discharge voltage (ca. 4.7 V). However, the interface between the LiNi0.5Mn1.5O4 cathode and the electrolyte is a great concern because of the decomposition of the electrolyte on the cathode surface at high operational potentials. To build a stable and functional protecting layer of Li3PO4 on LiNi0.5Mn1.5O4 to avoid direct contact between the active materials and the electrolyte is the emphasis of this study. Li3PO4-coated LiNi0.5Mn1.5O4 is prepared by a solid-state reaction and noncoated LiNi0.5Mn1.5O4 is prepared by the same method as a control. The materials are fully characterized by XRD, FT-IR, and high-resolution TEM. TEM shows that the Li3PO4 layer (<6 nm) is successfully coated on the LiNi0.5Mn1.5O4 primary particles. XRD and FT-IR reveal that the synthesized Li3PO4-coated LiNi0.5Mn1.5O4 has a cubic spinel structure with a space group of Fd3m, whereas noncoated LiNi0.5Mn1.5O4 shows a cubic spinel structure with a space group of P4(3)32. The electrochemical performance of the prepared materials is characterized in half and full cells. Li3PO4-coated LiNi0.5Mn1.5O4 shows dramatically enhanced cycling performance compared with noncoated LiNi0.5Mn1.5O4.

Keywords: Li3PO4; LiNi0.5Mn1.5O4; interfaces; lithium-ion batteries; solid-state reactions.