Dual-responsive polymer-coated iron oxide nanoparticles for drug delivery and imaging applications

Abstract

We reported the synthesis and characterization of dual-responsive poly(N-isopropylacrylamide-acrylamide-chitosan) (PAC)-coated magnetic nanoparticles (MNPs) for controlled and targeted drug delivery and imaging applications. The PAC-MNPs size was about 150nm with 70% iron mass content and excellent superparamagnetic properties. PAC-MNPs loaded with anti-cancer drug doxorubicin showed dual-responsive drug release characteristics with the maximum release of drugs at 40°C (∼78%) than at 37°C (∼33%) and at pH of 6 (∼55%) than at pH of 7.4 (∼28%) after 21 days. Further, the conjugation of prostate cancer-specific R11 peptides increased the uptake of PAC-MNPs by prostate cancer PC3 cells. The dose-dependent cellular uptake of the nanoparticles was also significantly increased with the presence of 1.3T magnetic field. The nanoparticles demonstrated cytocompatibility up to concentrations of 500μg/ml when incubated over a period of 24h with human dermal fibroblasts and normal prostate epithelial cells. Finally, pharmacokinetic studies indicated that doxorubicin-loaded PAC-MNPs caused significant prostate cancer cell death at 40°C than at 37°C, thereby confirming the temperature-dependent drug release kinetics and in vitro therapeutic efficacy. Future evaluation of in vivo therapeutic efficacy of targeted image-guided cancer therapy using R11-PAC-MNPs will reinforce a significant impact of the multifunctional PAC-MNPs on the future drug delivery systems.

Keywords: Chitosan; Dual-responsiveness; Iron oxide magnetic nanoparticles; Poly(N-isopropylacrylamide); Prostate cancer.