Design and fabrication of nanoscale semiconductors with regulatable morphology or structure has attracted tremendous interest due to the dependency relationship between properties and architectures. Two types of SrTiO3/TiO2 nanocomposites with different morphologies and structures have been fabricated by controlling the kinetics of hydrothermal reactions. One is TiO2 nanotube arrays densely wrapped by SrTiO3 film and the other is SrTiO3 nanospheres distributed on the top region of TiO2 nanotube arrays, which has been firstly fabricated. It has been found that the photoelectrochemical performances of these heterostructures are crucially dominated by their architectures. Heterostructured SrTiO3/TiO2 nanotube arrays were fabricated by traditional method in the absence of NaOH and they exhibited higher photoelectrochemical performance than pure TiO2 nanotube arrays. However, the compact SrTiO3 coating film on the sidewalls of TiO2 nanotube arrays could inevitably destroy the tubular structures of TiO2 and thus go against the vectorial transport of electrons. Interestingly, when excess NaOH was added into the growth solution, SrTiO3 nanospheres would be rationally grafted on the top of TiO2 nanotube arrays, which could preserve the tubular structures of TiO2, and thus further improve the photoelectrochemical performance.
Keywords: Heterostructure; Morphology modulation; One-dimensional; Photoelectrochemical.
Copyright © 2013 Elsevier Inc. All rights reserved.