The μ-(oxo)bis[tetra-tert-butylphthalocyaninato] aluminum(III) [(tBu)4PcAl]2O films with the crystallites oriented preferably in one direction were obtained via chemical transformation of tetra-tert-butylsubstituted chloroaluminum(III) phthalocyanine (tBu)4PcAlCl film upon its annealing in magnetic field. A comparative analysis of the influence of post-deposition annealing process without and under applied magnetic field of 1 T, on the orientation and morphology of (tBu)4PcAlCl and [(tBu)4PcAl]2O films, has been carried out by the methods of UV-vis, Infrared and Raman spectroscopies, XRD as well as atomic force microscopy. The formation of [(tBu)4PcAl]2O films with elongated crystallites having preferential orientation was observed upon heating of the films in magnetic field while annealing without magnetic field under the same conditions does not demonstrate any effect on the structure and morphology of these films. The reasons of the sensitivity of this reaction to the presence of such magnetic field is discussed and studied by electronic paramagnetic resonance spectroscopy.