Herein a comparative study of five nanocrystalline cerium oxides (CeO(2-delta)) synthesised by different methods and calcined at 500 degrees C is reported. XRPD analysis showed that stoichiometry parameter delta, crystallite size/strain and lattice constant were only slightly affected by the method utilized. All ceria nanoparticles are nearly spherical in shape with faceted morphology, free of defects and with a relatively uniform size distribution. The average microstrain was found to be approximately 10 times higher than that of bulk counterpart. The absorption edge of nanocrystalline materials was shifted towards a higher wavelengths (red shift) in comparison with bulk counterpart, and band gap values were in the range 2.7-3.24 eV (3.33 eV for bulk counterpart).