We performed a co-condensation reaction between aromatic aldehyde and aromatic diamine monomers on a highly oriented pyrolytic graphite surface either at a solid/liquid interface at room temperature or in low vacuum with moderate heating. With this simple and moderate methodology, we have obtained surface-confined 2D covalent organic frameworks (COFs) with few defects and almost entire surface coverage. The single crystalline domain can extend to more than 1 μm(2). By varying the backbone length of aromatic diamines the pore size of 2D surface COFs is tunable from ∼1.7 to 3.5 nm. In addition, the nature of the surface COF can be modified by introducing functional groups into the aromatic amine precursor, which has been demonstrated by introducing methyl groups to the backbone of the diamine. Formation of small portions of bilayers was observed by both scanning tunneling microscopy (STM) and AFM, which clearly reveals an eclipsed stacking manner.