For improvement of the processing and gaining uniformity texture structure and performance of direct chill cast CCAA 5052 aluminum alloy band after first hot rolling with different reduction, the material was annealed at 454 degrees C and then cold rolling with different reduction was conducted, the texture at surface, quarter and center layer of the sample was tested and examined by X-ray diffraction method, the data calculated using special software and the difference of texture at surface, quarter and center layer was analyzed. There existed an elevated gradient of intensity from surface layer to center layer after cold rolled with less than or equal to 40% reduction, The main texture of beta is stronger mainly due to transformation from remainder exposure, while the goss and remainder is infirm, the state of texture at each layer is close to each other after cold rolling with reduction high than 56.1%.