Objective: The objective of this in vitro study was to evaluate the immediate and short-term effects of laser neodymium-doped yttrium aluminum garnet (Nd:YAG) irradiation and in-office desensitizing treatment on dentin tubule occlusion.
Background data: Literature shows a lack of long-lasting treatments for dentin hypersensitivity.
Methods: Forty-eight dentin slabs (4×4×2 mm) were ground flat, polished, and treated with 27% ethylenediaminetetraacetic acid (EDTA) to open the dentinal tubules. Specimens were randomly divided into the following experimental groups (n=12): Group 1: Control (no treatment); Group 2: Nd:YAG laser irradiation (100 mJ, 85 J/cm(2) per pulse with a quartz fiber of 400 μm, in scanning movements); Group 3: In-office prophylaxis with pumice; Group 4: In-office Colgate Sensitive Pro-Relief™ Desensitizing Paste. Treatments were performed according to the manufacturer's instructions. After treatment, the specimens were submitted to a sequence of erosive and abrasive challenges, twice a day for 5 days. The specimens were qualitatively and quantitatively evaluated by scanning electron microscopy immediately after treatment and after 4 and 5 days. The response variable was the amount of occluded dentin tubules per area, determined by three different examiners with the use of visual criteria, with a standardized grade created in the PowerPoint program. Data were compared with ANOVA and Tukey's test, considering a 5% significance level.
Results: Immediately after treatment, a reduction in the number of opened dentin tubules was observed for the laser group when compared with the control group (p<0.05). After the experimental procedures, there were no quantitative differences between the amount of opened dentin tubules for all groups; however, micrographs showed some qualitative tubule occlusion for the laser group after the erosive/abrasive challenge.
Conclusions: only laser irradiation was capable of immediately sealing the dentinal tubules; however, none of the treatments showed efficacy in maintaining tubule occlusion after the chemical and mechanical challenges.