In the present work, the influence of different environments on the fatigue crack growth behaviour of 12% Cr steam turbine blade steel is investigated. Fatigue crack growth rates (FCGRs) in the near threshold regime are measured with ultrasonic fatigue testing technique. Fatigue tests are performed in vacuum, air and different aqueous environments with defined chloride and oxygen content. Furthermore, the influence of different stress ratios is investigated. It is found that crack propagation is not necessarily enhanced with increasing corrosiveness. In the aqueous environments, the FCGRs below 10⁻⁸ m/cycle are lower than in air. The threshold stress intensity factor ranges are higher or equal. Observation of the fracture surfaces shows oxide formation and partly intergranular fracture for specimens tested in aqueous environments. Crack closure effects seem to be responsible for this unexpected behaviour.
Keywords: 12% Cr steel; Corrosion fatigue; Fatigue crack growth; Threshold stress intensity; Ultrasonic fatigue.