The use of CO2 for scaffold fabrication in tissue engineering was popularized in the mid-1990 s as a tool for producing polymeric foam scaffolds, but had fallen out of favor to some extent, in part due to challenges with pore interconnectivity. Pore interconnectivity issues have since been resolved by numerous dedicated studies that have collectively outlined how to control the appropriate parameters to achieve a pore structure desirable for tissue regeneration. In addition to CO2 foaming, several groups have leveraged CO2 as a swelling agent to impregnate scaffolds with drugs and other bioactive additives, and for encapsulation of plasmids within scaffolds for gene delivery. Moreover, in contrast to CO2 foaming, which typically relies on supercritical CO2 at very high pressures, CO2 at much lower pressures has also been used to sinter polymeric microspheres together in the presence of cells to create cell-seeded scaffolds in a single step. CO2 has a number of advantages for polymer processing in tissue engineering, including its ease of use, low cost, and the opportunity to circumvent the use of organic solvents. Building on these advantages, and especially now with the tremendous precedent that has paved the way in defining operating parameters, and making the technology accessible for new groups to adapt, we invite and encourage our colleagues in the field to leverage CO2 as a new tool to enhance their own respective unique capabilities.