Nanometre sized particles of terbium and erbium co-doped yttrium oxysulfide up-converting phosphors were prepared by a urea homogeneous-precipitation method. Results from X-ray powder diffraction (XRPD), scanning electron microscopy (SEM) and photoluminescence spectroscopy studies on the microstructure and luminescent properties of the materials are reported. Upconversion emission was observed from the Er(3+) cations when particles were excited with laser light of 632.8 nm wavelength. Under these conditions no interactions between the Er(3+) cations and the Tb(3+) cations were observed. In contrast there was evidence from the Stokes emission of the Er(3+) cations under 254 nm excitation for an interaction between the Er(3+) and Tb(3+) cations reducing intensity of the latter's blue and green emission bands by cross relaxation processes.