Investigation of microstructure, mechanical properties and cellular viability of poly(L-lactic acid) tissue engineering scaffolds prepared by different thermally induced phase separation protocols

Abstract

Two thermally induced phase separation (TIPS) methods have been used to fabricate biodegradable poly(L-lactic acid) (PLLA) tissue engineering scaffolds each with fibrous (F-TIPS) and porous (P-TIPS) microstructures. Three levels of PLLA concentration (3, 5 and 7 wt%) were employed in each fabrication method and both wet and dry specimens were studied. Simple compression testing revealed that an elastic-plastic representation of the mechanical behavior was possible for all specimens. Both elastic and plastic moduli were higher for the P-TIPS, for higher polymer concentration, and might be somewhat higher for dry as opposed to wet specimens. For F-TIPS specimens, permanent deformation occurred successively during cyclic deformation but a "memory effect" simplified the behavior. Although F-TIPS microstructure better resembled the natural extracellular matrix, human osteosarcoma fibroblast cells showed more consistent viability in the P-TIPS scaffolds under our unloaded test protocols. Biodegradation in cell culture medium resulted in a decreased elastic moduli for F-TIPS specimens. Information presented regarding the microstructure, mechanical properties and cell viability of these PLLA scaffolds that should help reduce the number of iterations involved in developing tissue engineering products.