Multifunctional L1(0) -Mn(1.5)Ga films with ultrahigh coercivity, giant perpendicular magnetocrystalline anisotropy and large magnetic energy product

Abstract

A new kind of multifunctional L1(0) -Mn(1.5)Ga film is demonstrated for the first time. These MBE-grown epitaxial films exhibit pronounced magnetic properties at room temperature, including ultrahigh perpendicular coercivity up to 42.8 kOe, giant perpendicular magnetic anisotropy with a maximum of 21.7 Merg/cm(3) and large magnetic energy products up to 2.60 MGOe, which allow various applications in ultrahigh density recording, spintronics, and permanent magnets.