Objective: To evaluate a new biodegradable copolymer calcium sulfate/poly amino acid (CS/PAA) as a graft substitute for the repair of the surgically created cancellous bone defects in rabbits and its biological properties in vivo.
Materials and methods: Cancellous bone defects were created by drilling holes in the unilateral lateral aspect of the femoral condyle of New Zealand white rabbits. Three groups were assigned: Group A rabbits were grafted with 80% CS/PAA and group B rabbits were grafted with 95% CS/PAA as two treatment groups; group C was sham-operation control group. To study the osteogenic capability in vivo, specimens were harvested at 4, 8, 12, and 16 weeks after implantation and were evaluated by gross assessment, X-ray, histological examination, and histomorphometry. In order to identify the molecular mechanism of bone defect repair, the expression of bone morphogenetic protein-2 (BMP-2) and vascular endothelial growth factor (VEGF) was detected using Western blot at 4 weeks.
Results: Group A and group B showed more vigorous and rapid repair leading to regeneration of cancellous bone than sham-operation control group on gross observation, radiology, and histomorphometry. There was no significant difference between groups A and B. Morphological observation and histological examination showed that the copolymers degraded in sync with the new bone formation process. The expression of BMP-2 and VEGF in implantation groups was higher than that in control group by western blot.
Conclusion: These findings demonstrated that the novel biodegradable copolymers can repair large areas of cancellous bone defects. With its controllable degradation rate, it suggests that CS/PAA may be a series of useful therapeutic substitute for bone defects.
Keywords: Biodegradable; bone defects; graft substitute; polymer.