Modulation of cellular responses on engineered polyurethane implants

Abstract

An in vivo rat cage implant system was used to study the effect of polyurethane surface chemistries on protein adsorption, macrophage adhesion, foreign-body giant cell formation (FBGCs), cellular apoptosis, and cytokine response. Polyurethanes with zwitterionic, anionic, and cationic chemistries were developed. The changes in the surface topography of the materials were determined using atomic force microscopy and the wettability by dynamic contact angle measurements. The in vitro protein adsorption studies revealed higher protein adsorption on cationic surfaces when compared with the base, while adsorption was significantly reduced on zwitterionic (**p < 0.01) and anionic (*p < 0.05) polyurethanes. Analysis of the exudates surrounding the materials revealed no differences between surfaces in the types or levels of cells present. Conversely, the proportion of adherent cells undergoing apoptosis, as determined by annexin V-FITC staining, increased significantly on anionic followed by zwitterionic surfaces (60 + 5.0 and 38 + 3.7%) when compared with the base. Additionally, zwitterionic and anionic substrates provided decreased rates of macrophage adhesion and fusion into FBGCs, whereas cationic surfaces promoted macrophage adhesion and FBGC formation. Visualization of the F-actin cytoskeleton by Alexa Fluor 488 phalloidin showed a significant delay in the cytoskeletal fusion response on zwitterionic and the anionic surfaces. The real-time polymerase chain reaction (PCR) analysis of proinflammatory cytokines (tumor necrosis factor (TNF)-α and interleukin (IL)-10) and pro-wound healing cytokines (IL-4 and TGF-β) revealed differential cytokine responses. Cationic substrates that triggered stimulation of TNF-α and IL-4 were associated with more spread cells and higher FBGCs, whereas zwitterionic and anionic substrates that suppressed these cytokines levels were associated with less spread cells and few FBGCs. These studies have revealed that zwitterionic and anionic polyurethane surface chemistries can not only reduce nonspecific adhesion, fusion, and inflammatory events but also effectively promote cellular apoptosis in vivo.