The fibrous scaffolds are promising for tissue engineering applications because of their close structural resemblance with native extracellular matrix. Additionally, the chemical composition of scaffold is also an important consideration as they have significant influences on modulating cell attachment, morphology and function. In this study, chitosan-tripolyphosphate (TPP) non-woven fibrous scaffolds were prepared through wetspinning process. Interestingly, at physiological pH these scaffolds release phosphate ions, which have significant influences on cellular function. For the first time, cell viability in presence of varying concentration of sodium TPP solution was analyzed and correlated with the phosphate release from the scaffolds during 30 days incubation period. In vitro degradation of the chitosan-TPP scaffolds was higher than chitosan scaffolds, which may be due to decrease in crystallinity as a result of instantaneous ionic cross-linking during fiber formation. The scaffolds with highly interconnected porous structure present a remarkable cytocompatibility for cell growing, and show a great potential for tissue engineering applications.