The field-emission properties of SnO(2):WO(2.72) hierarchical nanowire heterostructure have been investigated. Nanoheterostructure consisting of SnO(2) nanowires as stem and WO(2.72) nanothorns as branches are synthesized in two steps by physical vapor deposition technique. Their field emission properties were recorded. A low turn-on field of ~0.82 V/μm (to draw an emission current density ~10 μA/cm(2)) is achieved along with stable emission for 4 h duration. The emission characteristic shows the SnO(2):WO(2.72) nanoheterostructures are extremely suitable for field-emission applications.
© 2011 American Chemical Society