Aim: To evaluate the effect of luting agent and fibreglass post design on bond strength to root dentine at different depths within the canal.
Methodology: Ninety single-rooted teeth were root filled and prepared to receive either a parallel-sided and serrated fibreglass post (Reforpost no. 2) or a tapered and smooth fibreglass post (Exato Cônico). The posts were cemented with the following resin cements: dual-cured resin cement (Rely X ARC), two self-adhesive resin cements (Rely X Unicem and MaxCem) and a self-cured resin cement (Cement-Post). The roots were cross-sectioned to obtain two 1-mm-thick discs for each cervical, middle and apical third of the prepared root portion. The posts were submitted to a micropush-out test at a speed of 0.5 mm min(-1), and the bond strength values (MPa) were submitted to anova in a split-plot arrangement and Tukey's test (P < 0.05).
Results: The RelyX Unicem demonstrated significantly higher bond strength values (P < 0.001) along the root dentine. The RelyX ARC and Cement-Post had similar bond strength values in the cervical third; however, the bond strength decreased significantly (P < 0.001) in an apical direction for the RelyX ARC. Significantly lower bond strength values (P < 0.001), irrespective of canal region, were found for MaxCem cement. The bond strength was similar for both post configurations irrespective of the resin cement and canal region.
Conclusions: The retention of glass fibre posts remained unaffected by surface roughness but was influenced by resin cement type. The self-adhesive cement RelyX Unicem yielded a significantly greater (P < 0.001) bond strength value when cementing the fibreglass posts.
© 2011 International Endodontic Journal.