A complete set of elastic, piezoelectric, and dielectric constants of [011](c) poled multidomain 0.24Pb(In(1/2)Nb(1/2))O(3)-0.46Pb(Mg(1/3)Nb(2/3))O(3)-0.30PbTiO(3) ternary single crystal has been determined using resonance and ultrasonic methods and the temperature dependence of the dielectric permittivity has been measured at 3 different frequencies. The experimental results revealed that this [011](c) poled ternary single crystal has very large transverse piezoelectric coefficient d(32) = -1693 pC/N, transverse dielectric constant ε(11)/ε(0) ~ 7400 and a high electromechanical coupling factor k(32) ~ 90%. In addition, its coercive field is 2 times of that of the corresponding binary 0.7Pb(Mg(1/3)Nb(2/3))O(3)-0.30PbTiO(3) single system with much better temperature stability. Therefore, the crystal is an excellent candidate for transverse mode electromechanical devices.