Selective photocatalytic oxidation of alcohols to aldehydes in water by TiO2 partially coated with WO3

Abstract

Semiconductor TiO(2) particles loaded with WO(3) (WO(3)/TiO(2)), synthesized by impregnation of tungstic acid followed by calcination, were used for photocatalytic oxidation of alcohols in water with molecular oxygen under irradiation at λ>350 nm. The WO(3)/TiO(2) catalysts promote selective oxidation of alcohols to aldehydes and show higher catalytic activity than pure TiO(2). In particular, a catalyst loading 7.6 wt % WO(3) led to higher aldehyde selectivity than previously reported photocatalytic systems. The high aldehyde selectivity arises because subsequent photocatalytic decomposition of the formed aldehyde is suppressed on the catalyst. The TiO(2) surface of the catalyst, which is active for oxidation, is partially coated by the WO(3) layer, which leads to a decrease in the amount of formed aldehyde adsorbed on the TiO(2) surface. This suppresses subsequent decomposition of the aldehyde on the TiO(2) surface and results in high aldehyde selectivity. The WO(3)/TiO(2) catalyst can selectively oxidize various aromatic alcohols and is reusable without loss of catalytic activity or selectivity.