We report the effect of pressing light-absorbing layers on the performance of polymer solar cells. The light-absorbing active layer was prepared on the transparent conducting oxide coated substrates from solutions that contain a mixture of regioregular poly(3-hexylthiophene) and soluble fullerene molecules. The active layers were pressed using a home-built micro-press system by controlling temperature and pressure, followed by the top electrode deposition. The surface of the active layers pressed was examined using atomic force microscope, while the photovoltaic characteristics of devices were measured under simulated solar light illumination (air mass 1.5 G, 100 mW/cm2). Results showed that the dark current of devices was noticeably increased by pressing the active layer without respect to the pressing temperature. The highest power conversion efficiency was achieved for the device with the active layer pressed under 10 kgf at 70 degrees C. The result was explained in terms of surface morphology and thermophysical effect.