This paper introduces how TiO2 film was prepared on pure titanium by anodic oxidation. Surface morphology and composition of the oxide film were analyzed by SEM coupled with EDAX. The deposition ability of hydroxyapatite of the anodized titanium in simulated body fluid (SBF) at 37 degrees C was evaluated. The results indicated that the oxide film was rough and honeycomb holes, connecting with each other, could be found on the surface. The holes with the diameter of 1-2 microm were distributed uniformly, which was typical for anodic oxidation. After alkaline treatment, hydroxyapatite deposition on the oxidized specimens in SBF was improved significantly.