Synthesis and characterization of nano-pore thallium (III) ion-imprinted polymer as a new sorbent for separation and preconcentration of thallium

Abstract

Thallium (III) ion-imprinted polymer (IIP) particles were synthesized by preparing the ternary complex of thallium (III) ions with 5,7-dichloroquinoline-8-ol (DCQ) and 4-vinylpyridine (VP). Thermal copolymerization with methyl methacrylate (functional monomer, MMA) and ethyleneglycoldimethacrylate (cross-linking monomer, EGDMA) was then performed in the presence of acetonitrile (porogen) and 2,2- azobisisobutyronitrile(initiator, AIBN). The imprinted ion was removed from polymer by stirring of the above particles with 5M HNO(3) to obtain the leached IIP particles. Moreover, control polymer (CP) particles were similarly prepared without the thallium (III) ions. The unleached and leached IIP particles were characterized by surface area analysis (BET), X-ray diffraction (XRD), Fourier transform infra-red spectroscopy (FT-IR), thermo gravimetric analysis (TGA) and scanning electron microscopy (SEM). The preconcentration of thallium (III) from aqueous solution was studied during rebinding with the leached IIP particles as a function of pH, the weight of the polymer material, the uptake and desorption times, the aqueous phase and the desorption volumes. Electrothermal atomic absorption spectrometry (ETAAS) was employed for determination of thallium in aqueous solution. The limit of detection for the method was 0.02 ng mL(-1), while the relative standard deviation for five replicates was 2.6%.