Both titanium nitride (TiN) and titanium aluminum nitride (TiAlN) have shown great wear resistance potential in metallic medical devices as protective, hard thin film coatings. In the present study, the effects of TiN and TiAlN coating layers on the wear performance of Ti-6Al-4V were compared and analyzed. TiN and TiAlN coatings with a thickness of 3 microm were deposited by a cathodic vacuum arc ion plating technique on the surface of Ti-6Al-4V. Wear tests were conducted by using a pin-on-disk-type tribotester with a point contact self-mating pair in a linear reciprocal motion. A sliding distance of 20 mm per cycle at 1 Hz was used under a load of 15 N under ambient conditions with no lubricant. The wear resistance of TiN and TiAlN coatings is superior to that of uncoated Ti-6Al-4V at the early stage of sliding contact. Until a measurable amount of wear was detected, the number of sliding cycles of the TiAlN coating pair was longer than TiN. After the first detection of wear from the coating layers, the rate of wear of the TiN coating pairs was significantly higher than that of TiAlN (p < 0.05), and it was close to that of the uncoated pairs. In conclusion, the TiAlN coating is superior to TiN from the viewpoint of wear resistance under the test conditions used in this study.