The ferroelectric, dielectric, elastic, piezoelectric, and electromechanical properties of tetragonal Pb(In(12)Nb(12))O(3)-Pb(Mg(13)Nb(23))O(3)-PbTiO(3) (PIN-PMN-PT) crystals were investigated. The single domain piezoelectric coefficients d(33), d(15), and d(31) were found to be 530, 2350, and -200 pCN, respectively, with electromechanical coupling factors k(33), k(15), and k(31) being on the order of 0.84, 0.85, and 0.58. The mechanical quality factor Q for longitudinal mode was found to be >700, with high coercive field (E(c)) being on the order of 10 kVcm. The temperature and dc bias electric-field characteristics of single domain tetragonal PIN-PMN-PT crystals were also investigated. In contrast to [001] oriented domain engineered rhombohedral crystals, tetragonal PIN-PMN-PT crystals exhibited broader temperature usage range and higher thermalelectric field stability, with improved coercive field and mechanical quality factor.