Single crystals of quasi-one-dimensional bromo-bridged Ni-Pd mixed-metal complexes with 2S,3S-diaminobutane (bn) as an in-plane ligand, [Ni(1-x)Pd(x)(bn)(2)Br]Br(2), were obtained by using an electrochemical oxidation method involving mixed methanol/2-propanol (1:1) solutions containing different ratios of [Ni(II)(bn)(2)]Br(2) and [Pd(II)(bn)(2)]Br(2). To investigate the competition between the electron-correlation of the Ni(III) states, or Mott-Hubbard states (MH), and the electron-phonon interaction of the Pd(II)-Pd(IV) mixed valence states, or charge-density-wave states (CDW), in the Ni-Pd mixed-metal compounds, X-ray structure analyses, X-ray oscillation photograph, and Raman, IR, ESR, and single-crystal reflectance spectra were analyzed. In addition, the local electronic structures of Ni-Pd mixed-metal single crystals were directly investigated by using scanning tunneling microscopy (STM) at room temperature and ambient pressure. The oxidation states of [Ni(1-x)Pd(x)(bn)(2)Br]Br(2) changed from a M(II)-M(IV) mixed valence state to a M(III) MH state at a critical mixing ratio (x(c)) of approximately 0.8, which is lower than that of [Ni(1-x)Pd(x)(chxn)(2)Br]Br(2) (chxn = 1R,2R-diaminocyclohexane) (x(c) approximately 0.9) reported previously. The lower value of x(c) for [Ni(1-x)Pd(x)(bn)(2)Br]Br(2) can be explained by the difference in their CDW dimensionalities because the three-dimensional CDW ordering in [Pd(bn)(2)Br]Br(2) observed by using X-ray diffuse scattering stabilizes the Pd(II)-Pd(IV) mixed valence state more than two-dimensional CDW ordering in [Pd(chxn)(2)Br]Br(2) does, which has been reported previously.