Aim: To examine the effect of the application of an ethanol rinse before luting fibre posts to intraradicular dentine with etch-and-rinse adhesive systems by means of push-out bond strength evaluation and scanning electron microscopic (SEM) analysis.
Methodology: Fibre posts were luted to single-canal premolars using Dual Link as a luting agent in combination with a three-step (All Bond 2) or a two-step (One Step Plus) etch-and-rinse adhesive system, which were applied as per manufacturers' instructions (control) or with the additional rinse of ethanol on acid-etched dentine prior to the bonding procedures (experimental). Bonded specimens were sectioned into 1-mm-thick slabs and subjected to push-out bond strength testing. In addition, specimens from each group were processed for SEM analysis. Data were analysed by Kruskal-Wallis followed by Dunn's post hoc test at P = 0.05.
Results: Push-out bond strength of All Bond 2 was significantly increased if the adhesive was applied on ethanol-saturated dentine (P < 0.05), whilst no significant difference (P > 0.05) was detected amongst experimental and control groups for One Step Plus. Irrespective of the adhesive, the SEM analysis revealed good impregnation patterns when both bonding techniques were employed.
Conclusions: The use of the additional ethanol rinse on acid-etched dentine revealed higher bond strength of All Bond 2 when compared with the control application procedure, used in combination with a resin-based cement to lute fibre posts into the dowel space. However, no bond strength improvements were detected using One Step Plus. Further investigations are needed to develop a clinically applicable ethanol/bonding/luting technique.