The influence of magnetite (Fe(3)O(4)) nanoparticles on the rheological properties of kappa-, iota- and lambda-carrageenan gels has been investigated. Small amplitude oscillatory shear measurements were performed to study the effect of the presence of Fe(3)O(4) nanoparticles with particle sizes of ca. 10 nm on the gel properties, as a function of carrageenan type, carrageenan concentration and magnetite load. The formation of Fe(3)O(4) nanoparticles on the presence of biopolymer was observed to promote the gelation process and lead to stronger gels as indicated by an increase in the gel viscoelastic moduli and of the gelation temperature. This effect was more marked for kappa-carrageenan than for iota- and lambda-carrageenan and has been proposed to depend not only on Fe(3)O(4) concentration but also on the concentration of potassium ions. A mechanism based on the combined effect of Fe(3)O(4) nanoparticles and potassium ions was suggested, involving the adsorption of potassium ions on the negatively charged surface of the Fe(3)O(4) nanoparticles, thus leading to an increase of the potassium ion concentration within the "carrageenan cages" containing the magnetite. This would, therefore, promote more extensive biopolymer helical aggregation, thus resulting in the formation of a stronger kappa-carrageenan gel in the presence of Fe(3)O(4), as observed. Since iota- and lambda-carrageenan gels are known to be less sensitive to potassium ions concentration, the effect of precipitating Fe(3)O(4) within these biopolymers is reduced.