The role of transport and re-adsorption processes on the oxygen reduction reaction (ORR), and in particular on its selectivity was studied using nanostructured model electrodes consisting of arrays of Pt nanostructures of well-defined size and separation on a planar glassy carbon (GC) substrate. The electrochemical measurements were performed under controlled transport conditions in a double-disk electrode thin-layer flow-cell configuration; the model electrodes were fabricated by colloidal lithography techniques, yielding Pt nanostructures of well defined and controlled size and density (diameter: 140 or 85 nm, height: 20 or 10 nm, separation: from 1-2 to more than 10 diameters). The nanostructured model electrodes were characterized by scanning electron microscopy and electrochemical probing of the active surface area (via the hydrogen adsorption charge). The electrocatalytic measurements revealed a pronounced variation of the hydrogen peroxide yield, which increases by up to two orders of magnitude with increasing separation and decreasing size of the Pt nanostructures. Similar, though less pronounced effects were observed upon varying the electrolyte flow and thus the mass transport characteristics. These effects are discussed in a reaction model which includes (i) direct reduction to H(2)O on the Pt surface and (ii) additional H(2)O(2) formation and desorption on both Pt and carbon surfaces and subsequent partial re-adsorption and further reduction of the H(2)O(2) molecules on the Pt surface.