Biocompatible polycaprolactone (PCL) and hydroxyapatite (HA) were fabricated into nanofibrous scaffolds for the mineralization of osteoblasts in bone tissue engineering. PCL and PCL/HA nanofibrous surface were modified using oxygen plasma treatment and showing 0 degrees contact angle for the adhesion and mineralization of osteoblast cells. The fiber diameter, pore size and porosity of nanofibrous scaffolds were estimated to be 220-625 nm, 3-20 microm, and 87-92% respectively. The ultimate tensile strength of PCL was about 3.37 MPa and PCL/HA was 1.07 MPa to withstand the long term culture of osteoblasts on nanofibrous scaffolds. Human fetal osteoblast cells (hFOB) were cultured on PCL and PCL/HA surface modified and unmodified nanofibrous scaffolds. The osteoblast proliferation rate was significantly (p < 0.001) increased in surface-modified nanofibrous scaffolds. FESEM showed normal phenotypic cell morphology and mineralization occurred in PCL/HA nanofibrous scaffolds, HA acting as a chelating agent for the mineralization of osteoblast to form bone like apatite for bone tissue engineering. EDX and Alizarin Red-S staining indicated mineral Ca(2+) and phosphorous deposited on the surface of osteoblast cells. The mineralization was significantly increased in PCL/HA-modified nanofibrous scaffolds and appeared as a mineral nodule synthesized by osteoblasts similar to apatite of the natural bone. The present study indicated that the PCL/HA surface-modified nanofibrous scaffolds are potential for the mineralization of osteoblast for bone tissue engineering.
Copyright 2007 Wiley Periodicals, Inc.