Al-pillared montmorillonite clay minerals: low-pressure CO adsorption at room temperature

Atsushi Itadani; Masashi Tanaka; Takahiro Abe; Hideki Taguchi; Mahiko Nagao

doi:10.1016/j.jcis.2007.04.074

Al-pillared montmorillonite clay minerals: low-pressure CO adsorption at room temperature

J Colloid Interface Sci. 2007 Sep 15;313(2):747-50. doi: 10.1016/j.jcis.2007.04.074. Epub 2007 Jun 11.

Authors

Atsushi Itadani¹, Masashi Tanaka, Takahiro Abe, Hideki Taguchi, Mahiko Nagao

Affiliation

¹ Research Laboratory for Surface Science, Faculty of Science, Okayama University, 3-1-1 Tsushima-naka, Okayama 700-8530, Japan. itadani@cc.okayama-u.ac.jp

PMID: 17561068
DOI: 10.1016/j.jcis.2007.04.074

Abstract

Three kinds of Al-pillared montmorillonite clay minerals (AlPMON) ion-exchanged with cobalt(II), nickel(II), or copper(II) ions were prepared (abbreviated as CoAlPMON, NiAlPMON, or CuAlPMON, respectively). For the 673-K- and 873-K-treated samples, carbon monoxide (CO) adsorption measurement was performed at room temperature under an atmosphere of low CO pressure. The 873-K-treated CuAlPMON sample exhibited more efficient adsorption properties for CO molecules, in comparison with both-temperatures-treated CoAlPMON and NiAlPMON samples and the 673-K-treated CuAlPMON sample. In addition, irreversibly adsorbed CO was present only on the CuAlPMON sample that had been treated at 873 K; the sites responsible for strong CO adsorption were formed in the sample after the pretreatment at the higher temperature.