Well-aligned ZnO nanowires have been synthesized vertically on In0.2Ga0.8N, GaN, and Al0.25Ga0.75N substrates, using a catalyst-free carbon thermal-reduction vapor phase deposition method for the first time. The as-synthesized nanowires are single crystalline wurtzite structure, and have a growth direction of [0001]. Each nanowire has a smooth surface, and uniform diameter along the growth direction. The average diameter and length of these nanowires are 120-150 nm, and 3-10 )m, respectively. We suggest that the growth mechanism follow a self-catalyzing growth model. Excitonic emission peaked around 385 nm dominates the room-temperature photoluminescence spectra of these nanowires. The room-temperature photoluminescence and Raman scattering spectra show that these nanowires have good optical quality with very less structural defects.