Anodization of titanium in a fluorinated dimethyl sulfoxide (DMSO) and ethanol mixture electrolyte is investigated. The prepared anodic film has a highly ordered nanotube-array surface architecture. Using a 20 V anodization potential (vs Pt) nanotube arrays having an inner diameter of 60 nm and 40 nm wall thickness are formed. The overall length of the nanotube arrays is controlled by the duration of the anodization, with nanotubes appearing only after approximately 48 h; a 72 h anodization results in a nanotube array approximately 2.3 mum in length. The photoelectrochemical response of the nanotube-array photoelectrodes is studied using a 1 M KOH solution under both UV and visible (AM 1.5) illumination. Enhanced photocurrent density is observed for samples obtained in the organic electrolyte, with an UV photoconversion efficiency of 10.7%.