High-yield H-form trititanate nanotubes have been synthesized, and their structures have been characterized by using X-ray diffraction and high-resolution transmission electron microscopy. According to combined TGA/XRD studies, the nanotubes are not stable at high temperature. Thermal analysis suggests that the stoichiometry of the material is H(2)Ti(3)O(7).0.8H(2)O(abs). Conductivity measurements indicate that mainly protonic transport occurs at temperatures below 150 degrees C and that with increasing temperature and progressive breakdown of nanotubes and formation of crystalline TiO(2) phases protonic conductivity is lost, leaving only residual defect electronic conduction. The proton conductivity is ca. 5.5 x 10(-6) S cm(-1) at 300 K. The structural protons and trapped water were confirmed by solid-state NMR.