Structural characteristics of CeO(2)-ZrO(2)/TiO(2) (CZ/T) and V(2)O(5)/CeO(2)-ZrO(2)/TiO(2) (V/CZ/T) mixed oxide catalysts have been investigated using X-ray diffraction (XRD), BET surface area, Raman spectroscopy (RS), and high-resolution transmission electron microscopy (HREM) techniques. The CeO(2)-ZrO(2) (1:1 mole ratio) solid solution was deposited over a finely powdered TiO(2) support by a deposition precipitation method. A nominal 5 wt % V(2)O(5) was impregnated over the calcined (773 K) CZ/T mixed oxide carrier by a wet impregnation technique. The obtained CZ/T and V/CZ/T samples were further subjected to thermal treatments from 773 to 1073 K to understand the dispersion and temperature stability of these materials. In the case of CZ/T samples, the XRD results suggest the formation of different cubic and tetragonal Ce-Zr-oxide phases, Ce(0.75)Zr(0.25)O(2), Ce(0.6)Zr(0.4)O(2), Ce(0.5)Zr(0.5)O(2), and Ce(0.16)Zr(0.84)O(2) in varying proportions depending on the treatment temperature. With increasing calcination temperature from 773 to 1073 K, the intensity of the lines pertaining to cubic Ce(0.6)Zr(0.4)O(2) and Ce(0.5)Zr(0.5)O(2) phases increased at the expense of cubic Ce(0.75)Zr(0.25)O(2), indicating more incorporation of zirconia into the ceria lattice. The TiO(2) was mainly in the anatase form whose crystallite size also increased with increasing treatment temperature. A better crystallization and more incorporation of zirconia into the ceria lattice was noted when CZ/T was impregnated with V(2)O(5). However, no crystalline V(2)O(5) could be seen from both XRD and RS measurements. In particular, a preferential formation of CeVO(4) compound and an intense tetragonal Ce(0.16)Zr(0.84)O(2) phase were noted beyond 873 K. The HREM results indicate, in the case of CZ/T samples, a well-dispersed Ce-Zr-oxide of the size approximately 5 nm over the bigger crystals ( approximately 40 nm) of TiO(2) when treated at 873 K. The exact structural features of these crystals as determined by digital diffraction analysis of experimental images reveal that the Ce-Zr-oxides are mainly in the cubic fluorite geometry and the TiO(2) is in anatase form. A better crystallization of Ce-Zr-oxides ( approximately 8 nm) over the surface of bigger crystals of TiO(2) was noted at 1073 K. A further enhancement in the crystallite size and zirconia-rich tetragonal phase was noted in the case of V/CZ/T samples. Further, the structure of CeVO(4) formed was also clearly identified in conformity with XRD and RS results.