The influence of corrosion on the bond strength of different brazed joints commonly used in dentistry has been investigated by means of accelerated immersion tests in artificial saliva buffered at pH 2, and in Ringer's solution, both kept at 37 degrees C. Two Co-Cr base metal alloys were brazed with a gold and a non-precious alloy. After 60 days' immersion the tensile strength of the samples brazed with the gold alloy was dramatically reduced because of galvanic corrosion phenomena. The bond strength of the specimens brazed with the non-precious alloy was largely unaffected. Corrosion products rich in nickel were detected. The electrochemical characterization of the base metal alloys and brazing materials was performed by means of polarization curves in the two media investigated. High short circuit currents were only produced with the gold brazing materials.