Titania mesosized particles were obtained by TiCl4 hydrolysis in Aerosol OT/water/n-hexane microemulsion. These particles were incorporated in surfactant templated silica mesoporous materials of MCM-41 and MCM-50 structures. Results depended on the surfactant: hexadecyltrimethylammonium bromide templated materials retained the honeycomb structure with small modifications in their characteristics. The dodecyltrimethylammonium bromide templated material changed from honeycomb to lamellar structure when the titania particles were included, with dramatic changes in the structure characteristics. The didodecyldimethylammonium bromide templated lamellar structure was retained after TIO2 inclusion, with a slight increase in the specific area, pore diameter and pore walls thickness.