Fe-C-TiO(2) photocatalysts which contained the residue carbon (0.2-3.3 mass%) were prepared from a mixture of TiO(2) and FeC(2)O(4) through the heating at 673-1173 K in Ar. These photocatalysts did not show a high adsorption of phenol, but they were active in photo-Fenton reactions during decomposition of phenol under UV irradiation with addition of H(2)O(2). It was proved that Fe(2+) governed the photoactivity of Fe-C-TiO(2) photocatalysts, it decreased with heat-treatment temperature above 773 K. For comparison, Fe-TiO(2) photocatalyst was prepared by heating TiO(2) and FeC(2)O(4) at 823 K in air for 3h. Phenol decomposition was going much slower on Fe-TiO(2) photocatalyst in comparison with Fe-C-TiO(2), of which mechanism was different, on the former phenol was decomposed by the radical reaction, on the latter through a complex reaction with iron and intermediates of phenol decomposition. Therefore carbon-coating TiO(2) was found to be advantageous for mounting iron and its application for the phenol decomposition via photo-Fenton process.