Two new lamellar inorganic-organic magnesium silicates have been successfully synthesized by using sol-gel based processes under mild temperature conditions. The talc-organosilicates derived using two silylating agents as the silicon source, (i) 3-chloropropyltrimethoxysilane, and (ii) from the attachment of 5-amino-1,3,4-thiadiazole-2-thiol molecule to this precursor agent, yielded PhMg-Cl and PhMg-Tz phyllosilicates. These organoclays were characterized through elemental analyses, infrared spectroscopy, X-ray diffractometry, surface area, thermogravimetry, and carbon and silicon solid state nuclear magnetic resonance spectroscopy. The results confirmed the presence of organic moieties covalently bonded to the inorganic silicon sheet network of the 2:1 class of phyllosilicates, with a density of organic molecules of 6.6+/-0.1 and 2.7+/-0.2 mmol g(-1) anchored on the inorganic layer and with interlayer distances of 1158 and 1628 pm, respectively. The nuclear magnetic resonances results in the solid state are in agreement with the sequence of carbons distributed in the pendant chains of the original silylating agents and the silicon bonded to oxygen atoms or carbon atoms of the inorganic sheets, as expected for the organically functionalized phyllosilicates. The enhanced potential of the new compound PhMg-Tz as a multi property material was explored in adsorbing cations from aqueous solution. The basic sulfur and nitrogen centers attached to the pendant chains inside the lamellar cavity can coordinate mercury, by presenting an isotherm saturated at 0.19 mmol g(-1) of this heavy metal. The functionality of this organoclay-like material expresses its potential for heavy cation removal from an ecosystem.