The functional properties of three shrimp chitosan preparations with different degrees of deacetylation (75%, 87% and 96% DD) but with a constant molecular weight (about 810 kDa) were investigated. Chitosan with 75% DD had a 1.5 times higher water absorption, probably due to its 20% lower level of crystallinity. Membranes cast from this chitosan also exhibited 1.5 times more water absorption and 2 times higher permeability. However, chitosan with 87% and 96% DD had 1.5-2 times higher absorption of fat and the orange II dye. This is attributed to the higher content of positively charged amine groups in the polymer. Cast into membrane, chitosan of higher degree of deacetylation showed a higher tensile strength and a higher elongation at break, probably due to the higher level of crystallinity.