Investigation of the growth of CdSe nanocrystals ( approximately 160 atoms) to the uniquely stable size of 2 nm allows the monitoring of the crystallization process in semiconductor quantum dots. By using a combination of optical techniques, high-resolution transmission electron microscopy (HRTEM), and powder X-ray diffractometry (XRD), new phenomena were explored during the CdSe nanocrystal growth process, which involved significant morphological reconstruction and crystallization of the initially formed amorphous nanoparticles. During the crystallization, the absorption onset of the CdSe quantum dots blue shifted toward higher energies at 3 eV (414 nm), while the photoluminescence red shifted to lower energies. Furthermore, an apparent increasing Stokes shift was observed during the formation of small CdSe nanoparticles. On the other hand, the photoluminescence excitation spectra showed constant features over the reaction time. Additionally, results from HRTEM and XRD studies show that the CdSe nanoparticles were amorphous at early reaction stages and became better crystallized after longer reaction times, while the particle size remained the same during the crystallization process. These observations demonstrate the important role of the surface on the optical properties of small CdSe quantum dots and facilitated the spectroscopic monitoring of the crystallization process in quantum dots.