Glassy carbon (GC) has high potential to serve as a biomaterial in neural applications because it is biocompatible, electrochemically inert and can be incorporated in polyimide-based implantable devices. Miniaturization and applicability of GC is, however, thought to be partially limited by its electrical conductivity. For this study, ultra-conformable polyimide-based electrocorticography (ECoG) devices with different-diameter GC electrodes were fabricated and tested in vitro and in rat models. For achieving conformability to the rat brain, polyimide was patterned in a finger-like shape and its thickness was set to 8 µm. To investigate different electrode sizes, each ECoG device was assigned electrodes with diameters of 50, 100, 200 and 300 µm. They were electrochemically characterized and subjected to 10 million biphasic pulses-for achieving a steady-state-and to X-ray photoelectron spectroscopy, for examining their elemental composition. The electrodes were then implanted epidurally to evaluate the ability of each diameter to detect neural activity. Results show that their performance at low frequencies (up to 300 Hz) depends on the distance from the signal source rather than on the electrode diameter, while at high frequencies (above 200 Hz) small electrodes have higher background noises than large ones, unless they are coated with poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS).
Keywords: ECoG; conformability; glassy carbon; neural implants; poly(3,4-ethylenedioxythiophene) (PEDOT); polyimide; pyrolysis.