Effect of the Ratio of Magnetite Particle Size to Microwave Penetration Depth on Reduction Reaction Behaviour by H2

Ahmadreza Amini; Ko-Ichiro Ohno; Takayuki Maeda; Kazuya Kunitomo

doi:10.1038/s41598-018-33460-5

Effect of the Ratio of Magnetite Particle Size to Microwave Penetration Depth on Reduction Reaction Behaviour by H₂

Sci Rep. 2018 Oct 9;8(1):15023. doi: 10.1038/s41598-018-33460-5.

Authors

Ahmadreza Amini¹, Ko-Ichiro Ohno², Takayuki Maeda², Kazuya Kunitomo²

Affiliations

¹ Department of Materials Process Engineering, Graduate School of Engineering, Kyushu University, Kyushu, Japan. 3TE16031G@s.kyushu-u.ac.jp.
² Department of Materials Science and Engineering, Faculty of Engineering, Kyushu University, Kyushu, Japan.

Abstract

In this study, we investigated reduction of magnetite by H₂ during microwave irradiation. This process combines the advantages of microwave irradiation and using H₂ as a reducing agent to mitigate CO₂ emissions during the ironmaking process. Weight change measurements showed that a reduction of 75% was achieved after treatment under H₂ for 60 min. For better understanding of the effective parameters in microwave chemistry, scanning electron microscopy, combined with energy-dispersive X-ray spectroscopy (SEM-EDX), was performed, which demonstrated a greater reduction of large particles (>40 μm) than small particles. This behaviour could be attributed to the higher microwave absorption capability of large particles with a higher ratio of particle size to penetration depth (d/δ). Small particles behave as transparent material and are heated via conduction and/or convection; thus, there is no contribution from the catalytic effect of microwaves to the reduction reaction. Moreover, the reduction of Fe₃O₄ to Fe_0.94O, followed by transformation to Fe, seems to proceed from the surface toward the centre of the particle despite the volumetric microwave heating. This could be due to the higher gas accessibility of iron oxide on the particle surface than in the particle centre.