Highly luminescent MAPbI3 perovskite quantum dots with a simple purification process via ultrasound-assisted bead milling

Junya Enomoto; Ryota Sato; Masaaki Yokoyama; Taisei Kimura; Naoaki Oshita; Kazuki Umemoto; Satoshi Asakura; Akito Masuhara

doi:10.1039/d1ra08887d

Highly luminescent MAPbI₃ perovskite quantum dots with a simple purification process via ultrasound-assisted bead milling

RSC Adv. 2022 Feb 16;12(9):5571-5576. doi: 10.1039/d1ra08887d. eCollection 2022 Feb 10.

Authors

Junya Enomoto¹, Ryota Sato¹, Masaaki Yokoyama¹, Taisei Kimura¹, Naoaki Oshita¹, Kazuki Umemoto¹, Satoshi Asakura^{1

2}, Akito Masuhara^{1

3}

Affiliations

¹ Graduate School of Science and Engineering, Yamagata University 4-3-16, Jonan Yonezawa Yamagata 992-8510 Japan.
² Ise Chemicals Corporation 1-3-1, Kyobashi Chuo-ku Tokyo Japan.
³ Frontier Center for Organic Materials (FROM), Yamagata University 4-3-16, Jonan Yonezawa Yamagata 992-8510 Japan.

Abstract

Organic-inorganic hybrid lead halide perovskite quantum dots (QDs) have various excellent optical properties, and they have drastically enhanced the field of light-emitting diode (LED) research. However, red-emissive CH₃NH₃ (MA) PbI₃ QDs have worse optical properties compared with those of green-emissive MAPbBr₃ QDs due to their instability under high-moisture and high-temperature conditions. Therefore, it is quite difficult to prepare MAPbI₃ QDs with good optical properties via bottom-up methods using conditions involving high temperature and high-solubility solvents. On the other hand, top-down methods for preparing MAPbI₃ QDs under an air atmosphere have attracted attention; however, there are issues, such as PL emission with a wide FWHM being obtained due to the wide particle-size distribution. In this research, red-emissive MAPbI₃ QDs were prepared via an ultrasound-assisted bead milling (UBM) method, and the MAPbI₃ QDs were purified using various carboxylate esters. As a result, we solved the issue of the wide particle-size distribution unique to top-down methods via purifying the MAPbI₃ QDs, and they achieved the following excellent optical properties: a FWHM of 44 to 48 nm and a PLQY of over 60%. Notably, a fabricated LED device with MAPbI₃ QDs purified using methyl acetate showed a PL peak at 738 nm and a FWHM of 49 nm, resulting in an excellent EQE value of 3.2%.