Polytetrafluoroethylene (PTFE) membrane filters are widely used in low-load application areas, such as industrial cleanrooms, due to their low initial pressure drop. In this study, melt-blown (MB) nonwoven was introduced as a pre-filtration layer at the front end of a high-efficiency particulate air (HEPA) filter to improve the filter performance of the PTFE membrane. Pre-filtration reduces the average particle size, which reaches the PTFE membrane and reduces the dust load on the HEPA filters. A comparative analysis of the HEPA filters by composite MB and PTFE was conducted. Regarding the MB composite on the PTFE, low-weight and high-weight MB composites were effective in increasing dust filtration efficiency, and the dust loading capacity of the PTFE composite with high-weight MB increased by approximately three times that of the PTFE membrane. In addition, the filter was installed on an external air conditioner in an actual use environment and showed a high efficiency of 99.984% without a change in differential pressure after 120 days.
Keywords: HEPA filter; PTFE membrane; clean room; melt-blown; pre-filter.