Effect of the Type of Inorganic Binder on the Microstructure and Properties of AlSi7Mg Alloy Castings Made by Ablation Casting Technology

The results of studies on the effect that the type of binder and casting technology exert on the microstructure and properties of AlSi7Mg alloy castings are discussed in this paper. Comparative tests were carried out on three casting manufacturing technologies, i.e., conventional sand mould casting and cooling process, metal mould (die) casting, and sand mould casting with ablation breakdown of mould and cooling of castings. Moulds were made from four different sand mixtures with inorganic binders hardened by various technologies. The microstructure of test castings was examined at three different levels, i.e., in the upper part, central part, and lower part of each casting. The tensile test at room temperature was carried out in accordance with standards. The experimental results showed differences in the microstructure of castings. The differences resulted from changes in the crystallisation path due to the use of three different casting technologies, ensuring different rates of heat dissipation from castings; they were also due to the shape of castings. It has been shown that castings made by ablation technology are characterised by a high degree of the microstructure refinement (SDAS reduced by 18-30%), which gives higher strength properties than the properties of castings made in conventional sand moulds. Samples taken from castings made by the ablation technology in moulds with phosphate binder and microwave-hardened geopolymer binder were characterised by the mechanical properties comparable to gravity die castings.